AMS 6260-AISI 9310, AMS 6265-AISI E9310 Vacuum Melt

AMS 6260 – AISI 9310, AMS 6265 – AISI E9310 Vacuum Melt
STEELMAX Steel Story

니켈 + 크롬 + 몰리브덴 합금강재로
침탄 표면 경화강 (Carburizing case hardening) 으로 사용합니다.

높은 내충격, 내피로강도– High impact and fatigue strength.
좋은 경화능 — Good hardenability.

높은 심부 경도 — High core hardness
좋은 인성 — Good toughness properties 성질을 가집니다.

이런 성질을 이용해. 기어 (Gears), 크랭크축 (Crankshafts)
항공기용과 트럭 부품으로 사용되는 강재 입니다.

—————

AMS 6260 Standard Specification for Steel, Bars, Forgings, and Tubing,
1.2Cr – 3.2Ni – 0.12 Mo (0.07~0.13C) 규정이고

AMS 6260 Specification covers an aircraft-quality, low-alloy steel
in the form of bars, forgings, mechanical tubing, and forging stock으로

—————

AMS 6265 Standard Specification for Steel, Bars, Forgings, and Tubing,
1.2Cr – 3.2Ni – 0.12 Mo (0.07~0.13C).

AMS 6265 Specification covers a premium aircraft-quality, low-alloy steel
in the form of bars, forgings, mechanical tubing, and forging stock.

—————

AMS 6260, AMS 6265 의 차이는 premium 1단어 차이입니다.
그 차이는 AMS 6265 는 AMS 6260 과는 제조 방법과 달라

AMS6265 는, Vacuum Electrode Remelted 제조 방법은
강재의 청정성, 조직과 원소의 균질성을 향상 시키고,

결정립으 크기를 작게 해, 강을 성질을 높일 목적으로
응고된 강괴 (Ingot)를 다시 한번 용해하는 것으로,

용해를 진공 상태에서 해,
불순 Gas, 편석을 제거하는 방법입니다.

Standard		AISI 9310
Chemical composition (%)	Carbon (C)	0.08~0.13
	Manganese (Mn)	0.45~0.65
	Phosphorus (P)	0.025 max
	Sulfur (S)	0.025 max
	Silicon (Si)	0.15~0.35
	Nickel (Ni)	3.00~3.50
	Chromium (Cr)	1.00~1.40
	Molybdenum (Mo)	0.08~0.15
Normalized	Tensile Strength (MPa, min)	906.7
	Yield Strength (MPa, min)	570.9
	Elongation (%, min)	18.8
	Reduction area (%, min)	58.1
	Hardness (HB, min)	269
Annealed	Tensile Strength (MPa, min)	820.5
	Yield Strength (MPa, min)	439.9
	Elongation (%, min)	17.3
	Reduction area (%, min)	42.1
	Hardness (HB, min)	241

※ Case hardening steel (표면 경화강: 表面硬化鋼)
Low carbon steels and low carbon alloy steels of machine structural use
whose surfaces are hardened mainly by carburization hardening…….…JIS
Steels with a relatively low carbon content, which are intented for
carburizing or carbonitriding and subsequent hardening.
Such steels, after treatment, are characterized by a high hardness
surface layer and a tough ….…DIN-EN.

저탄소강 및 저탄소 합금강으로, 주로 침탄퀜칭에 의해 표면 경화 시킨 강
표면의 내마모성과 내피로성을 높이지만, 강재 내부의 인성을 유지 시킨 강재.
표면 경화 방법으로는 침탄 (Carburizing), 질화 (Nitriding), 침붕 (Boriding)이 있고
각각 탄소, 질소, 붕소를 강재 표면에 침투 시켜 경화 시키는 방법입니다.