JIS SB410 and G3103 Plate Tolerance on Thickness

JIS SB410 and G3103 Plate Tolerance on Thickness
STEELMAX Steel Story

SB410 은 탄소강 보일러 압력 용기용 강판 규격입니다.
중고온용 (Intermediate and elevated temperature) 으로

저온이나, 상온에서 사용하는 강판 규격이 아닙니다.
Normalizing (불림 열처리) 하는 경우는 SB410N으로

Steel Symbol SB410 에, “+N” 을 붙여서, 열처리 된 강판임을 분명히 합니다.
JIS SB410은 KS SB410 과 비슷하지만

JIS SB410 과 KS SB410 은 약간의 차이가 있습니다.
JIS SB410은 Killed Steel 으로만 제조합니다.

JIS G3103 SB410
Carbon (C)	t≤25	0.24 max
	25＜t≤50	0.27 max
	50＜t≤100	0.29 max
	100＜t≤200	0.30 max
Silicon (Si)		0.15~0.40
Manganese (Mn)		0.90 max
Phosphorus (P)		0.030 max
Sulfur (S)		0.030 max
Yield point (N/㎟)		225 min
Tensile strength (N/㎟)		410~550
Elongation (%)	6≤t≤50	21 min
	50＜t≤200	25 min

Thickness	Width
Thickness	W＜1600	1600≤w＜2000	2000≤w＜2500	2500≤w＜3150	3150≤w＜4000	4000≤w＜5000
6.00≤t＜6.30	+0.75	+0.95	+0.95	+1.25	+1.25	–
6.30≤t＜10.0	+0.85	+1.05	+1.05	+1.35	+1.35	+1.55
10.0≤t＜16.0	+0.85	+1.05	+1.05	+1.35	+1.35	+1.75
16.0≤t＜25.0	+1.05	+1.25	+1.25	+1.65	+1.65	+1.95
25.0≤t＜40.0	+1.15	+1.35	+1.35	+1.75	+1.75	+2.15
40.0≤t＜63.0	+1.35	+1.65	+1.65	+1.95	+1.95	+2.35
63.0≤t＜100	+1.55	+1.95	+1.95	+2.35	+2.35	+2.75
100≤t＜160	+2.35	+2.75	+2.75	+3.15	+3.15	+3.55
160≤t	+2.95	+3.35	+3.35	+3.55	+3.55	+3.95
※ minus 공차 0.25 mm
※ 폭 5000 mm 이상 협의
※ 공차 0 는 +측 허용차 0.25 mm 를 더함

Normalizing (불림)
Heat treatment consisting of austenitizing followed by air cooling.
The purposes of this operation are to eliminate the influence of pre-working,
to render the crystal grains finder and to improve their mechanical properties.

오스테나이트화 후 공기 중에서 냉각하는 열처리로
노말라이징 열처리의 목적은 강재 생산 앞 공정에서 받은 응력 (Stress)를 풀어주고
결정립을 미세화, 표준화 시켜, 기계적 성질을 향상 시키는 열처리를 말합니다.

※ Killed Steel
Steel sufficiently deoxidized with ferrosilicon, aluminium, and so on.
In the case of ingot casting, during the progress of solidification in a ingot mold,
it is gently solidified without generation of carbon monoxide,
being comparatively uniform, with little segregation and has no blow hole.
however, because of a shrinkage cavity is formed in the centre of upper part,
its yield is low, In the case of continuous casting, it is killed steel and,
comparing with an ingot casting, uniformity and yield better.
killed steel is further classified according to grain size or deoxidizer.

페로실리콘이나, 알루미늄 등으로 충분히 탈산한 강철로,
용탕이 응고 진행 중에 일산화탄소를 발생 시키지 않고,
조용히 응고해, 비교적 균질하고, 편석이 적고, 기포도 없지만
응고된 강괴 윗부분 중심으로부터, 수축공이 생겨, 회수율이
좋지 못한 단점이 있고, 결정 입도, 탈산제에 따라 세부적으로 더 분류됩니다.

※ 탄소강에서는 산소를 강철을 약하게 만드는 불순물로 보고
탈산제를 이용해 강 (Steel) 내부의 산소를 제거함.