S650MC, STRENX 650MC, High Yield Strength

S650MC, 1.8976, STRENX 650MC, High Yield Strength
STEELMAX Steel Story

S650MC 는, 열간 압연 냉간 성형용 고항복점 (high yield)
강판에 대한 DIN-EN 10492-2 규정 강재 입니다.

S650MC 는, 10492-2 규정 강재 중
alloy special steel grade, 합금강 재질입니다.

S650MC 규격의 이전 DIN
규격은 QStE650TM 으로 표기 됐었습니다.

DIN-EN 10492-2 규정 재질은 Hot-rolled products made of
high yield strength steels for cold forming

Part 2 : Delivery conditions for thermomechanically rolled steels 라는
긴 내용을 가지는 온라인 정밀 제어 열가공 압연으로 제조 된 강재 입니다.

S650MC 의, DIN-EN Material No. 1.8976,
SSAB trademark STRENX 650MC d입니다.

S650MC, 1.8976, Strenx 650MC
Mechanical properties (MPa, min)	Yield strength (MPa, min)	650
	Tensile strength (MPa, min)	700~880
	Elongation (%), t＜3	10
	Elongation (%), t≥3	12
Chemical composition (%)	Carbon (C)	0.12 max
	Manganese (Mn)	2.00 max
	Silicon (Si)	0.60 max
	Phosphorus (P)	0.025 max
	Sulfur (S)	0.015 max
	Aluminum (Al)	0.015 max
	Niobium (Nb)	0.09 max
	Vanadium (V)	0.20 max
	Titanium (Ti)	0.22 max
	Molybdenum (Mo)	0.50 max
	Boron (B)	0.005 max
	Nb+V+Ti	0.22 max

※ TMCP (열가공 제어)
A generic term for manufacturing methods carrying out air cooling or
enforced controlled cooling subsequent to the main process
of controlled rolling.
It includes the thermo-mechanical rolling and accelerated rolling,
but not when it is classical controlled rolling alone.
This is also called TMCP.

※ 열간 압연 강판 — KS
보통 약 800℃ 이상(통상 A3 변태점 이상)의 고온에서 압연된 강판.

※ 열간 압연 강판 — JIS
Hot rolled steel strip in coil by rolling mill, including the
steel strips in coil of thermo-mechanical control process(TMCP)

※ Yield Strength (항복강도 : 降伏强度)
Value of load strength which a specified permanent elongation
occurs in tensile test, expressed by dividing the load by original
sectional area of parallel portion.
the yield strength is used instead of yield point.

인장시험에서 규정된 영구 연신율을 일으킬 때의 하중을
평행부의 원단면적으로 나눈 값.
항복점을 항복강도로 사용하기도 합니다.

※ Alloy steel (합금강 : 合金鋼)
A Carbon steel to which is added a definite amount of one or more
elements other than carbon, in order to impart special properties
to the steel so that it can be used for specific purposes.

강의 성질을 향상 시키기 위해, 또는 소정의 성질을 구비 시키기 위해
합금 원소를 1 종 또는 2 종 이상을 합금 시킨 강.