A6061-T652, QQ-A-367, B247 Forged Aluminum

A6061 T652, QQ-A-367, B247 Forged Aluminum
STEELMAX Metal Story

A6061 은, Al-Mg-Si 합금으로
석출경화 알루미늄입니다.

가볍지만 어느 정도의 강도도 필요하고,
용접성도 있으면서 내식성도 요구되는

건축 용도, 가구용으로 사용됩니다.
A6061 은 열처리에 의해 강도를 높일 수 있는

열처리형 알루미늄 합금입니다.
A6061-T652 규격이면서

QQ-A-367 규격의 알루미늄 합금은
ASTM B247 Forgings, AMS 4127과 비교됩니다.

※ Temper T652 : Solution heat treated, compressed to a permanent
set of 1~5% for stress relief, and artificially aged

고용화 열처리 후, 1~5% 의 영구 변형을 주는 압축 가공을 하고
잔류 응력을 제거한 후, 인공 시효 경화 처리한 상태를 말합니다.

※ Temper T651 : Solution heat treated, stretched a controlled amount
(product dependent) for stress relief, and artificially aged
(no further straightening after stretching)

※ Solution heat treatment (용체화 처리/고용화 처리)
A process in which an alloy is heated to a suitable temperature and is held
at this temperature long enough to allow soluble constituents to enter into
solid solution where they are retained in a super-saturated state after quenching

합금을 적절한 온도로 가열하고 급랭 이후 과포화 상태로 존재하던
가용 성분이 고용체에 고용화 될 수 있도록 충분히 유지하는 공정을 말합니다.

※ Artificial ageing(precipitation heat treatment) : 인공시효 (석출 열처리)
A thermal treatment of an alloy at above room temperature to produce strengthening
by precipitation of soluble constituents from the super-saturated solid solution

과포화 고용체로부터 가용 성분의 석출에 의한 강화를 위하여
상온 이상에서 합금을 열처리 하는 것을 말합니다.

※ Stress Relief (응력 제거 어닐링 (풀림)
Heating to a suitable temperature, holding long enough
to reduce residual stresses and than cooling slowly
enough to minimized the development of new residual stresses.
A heat treatment in which the lock-up stresses in a bar caused
by cold working are removed by heating the bar closed to but
below the lower limit of the critical temperature range,
or to approximately 100℉ below the tempering temperature.

적당한 온도로 가열하고 균열화 한 후, 적절한 온도로 냉각함으로써
실질적인 조직의 변화 없이 내부 응력을 줄이고자 시행하는 열처리.

※ ASTM A247 Standard specification for aluminum and aluminum-alloy
die forgings, hand forgings, and rolled ring forgings

※ QQ-A-367 Specification covers aluminum alloyed forgings and hand forgings.

ASTM B247, 6061
Chemical composition (%)	Silicon (Si)	0.40~0.8
	Iron (Fe)	0.7 max
	Copper (Cu)	0.15~0.40
	Manganese (Mn)	0.15 max
	Magnesium (Mg)	0.8~1.2
	Chromium (Cr)	0.04~0.35
	Zinc (Zn)	0.25 max
	Titanium (Ti)	0.15 max
	Other each	0.05 max
	Other total	0.15 max
	Aluminum (Al)	remainder

ASTM B247, 6061 T6 or A6061-T652
Thickness		Direction	Tensile strength	Yield strength
Over	Through	Direction	MPa, min	MPa, min
	100.00	longitudinal	260	240
	100.00	long transverse	260	240
	100.00	short transverse	255	230
100.00	200.00	longitudinal	255	235
100.00	200.00	long/transverse	255	235
100.00	200.00	short transverse	240	220