15NiCuMoNb5-6-4, 1.6368, Flat, Elevated Temp.

15NiCuMoNb5-6-4, 1.6368, Flat, Elevated Temp.
STEELMAX Steel Story

15NiCuMoNb5-6-4, 1.6368 강재는 고온에서 사용하는
압력용기용, 용접용, 합금강재, Flat products, 열처리 강재입니다.

Fully Killed — 완전 탈산강이면서 fine grain 강재입니다.
normalizing and tempering or water quenching and tempering 열처리 강재입니다.

압력용기용으로 사용되어 -20~200℃ 온도 구역에서 사용되며
creep strength 와 온도 구역별 0.2% yield strength 규정이 있는 강재입니다.

※Fine grained steel (세립강 細粒鋼)
Steel with an austenitic grain size number is 5 or over … JIS

※ Fine grain steel
Steels which resist grain growth over a considerable temperature range,
when held at temperature for a reasonable length of time as is
customary in heat treatment of steel

※ Creep rupture test
Test measure the time to rupture, elongation after fracture,
reduction of area after fracture, etc. by holding test piece
at constant temperature and applying constant tensile force.
There are at times the cases where strain is measured during
creep rupture test or by interrupting test.

시험편을 일정한 온도로 유지하고 여기에 일정한 인장 하중을 가해,
파단 시간, 파단 연신율, 파단 단면 수축율 등을 측정하는 시험.
크리프 파단 시험 중 또는 시험을 중단하여
변형을 측정하는 경우도 있습니다.

※ Creep strength (크리프 강도)
Stress to cause specified strain in specified loading period of
time at constant temperature.
For example, the stress causing strain 1%, 0.1%, 0.01% in 1000h.
일정 온도하에서, 규정된 부하 시간에 규정된 변형이 생기는 응력.

예를 들면 1000 시간에 1%, 0.1% 또는 0.01%의 변형이
생기는 응력이 사용됩니다.

※ Steels for pressure vessels (압력용기용 강재 : 壓力容器用鋼材)
Steel products manufactured pressure vessels and high pressure
equipment which require strength, weldability and principally
toughness at a ordinary temperature.
They are generally used for the principal portions of pressure vessels.

압력 용기 및 고압 설비용으로서 고온 강도, 용접성 및 주로
상온에서의 인성을 중요시하여 제조 된 강재로
보통 압력 용기의 주요 부분에 사용됩니다.

1.6368, 15NiCuMoNb5-6-4
Chemical composition (%)	Carbon (C)	0.15~0.23
	Silicon (Si)	0.40 max
	Manganese (Mn)	1.00~1.50
	Phosphorus (P)	0.020 max
	Sulfur (S)	0.010 max
	Nitrogen (N)	0.012 max
	Chromium (Cr)	0.20 max
	Copper (Cu)	0.20 max
	Molybdenum (Mo)	0.45~0.60
	Nickel (Ni)	0.40~0.80
	Vanadium (V)	0.02 max
CVN, +QT	-20℃	27
	0℃	34
	20℃	40

1.6368		Reh, MPa, min.	Rm, MPa, min.	A (%, min.)
+NT	t≤40	460	610~780	16
	40＜t≤60	440	610~780	16
	60＜t≤100	430	600~760	16
+NT or +QT	100＜t≤150	420	590~740	16
+QT	150＜t≤200	410	580~740	16
Reh : Yield strength, Rm : Tensile strength, A : Elon.

Temp. ℃	Strength for 1% creep strain (MPa)		Creep rupture strength (MPa)
Temp. ℃	10,000h	100,000h	10,000h	100,000h
400	324	294	402	373
410	315	279	385	349
420	306	263	368	325
430	295	245	348	300
440	281	227	328	273
450	265	206	304	245
460	239	180	274	210
470	212	151	242	175
480	180	120	212	139
490	145	84	179	104
500	108	49	147	69