API 5L X52Q, Gr. L360Q, PSL2, Carbon SMLS QT

API 5L X52Q, Gr. L360Q, PSL2, Carbon SMLS QT
STEELMAX Steel Story

API 5L — Line Pipe 재질의 Grade X52Q는 52 ksi로
ksi 를, MPa 로 환산하면 360 MPa minimum 강도로

Quenching 910℃ and Tempering 640℃ 수준에서
열처리 된 Product Specification Level 2 (PSL2) API 규격 강재를

API 5L X52Q or L360Q 라고 Steel Grade로 표시합니다.
탄소강재 규격으로 Seamless (SMLS) 또는 용접 강관이 있습니다.

강관의 이음을 용접 방법으로 하기에 PCM, CEQ 규정이 있으며
CVN 충격 시험, NACE MR0175 / ISO 15156-2,

NACE MR0103 /ISO 17945 Hardness (HRC 22 max.),보증과
No Weld Repair, Fully killed & Fine grain steel 규정 적용 규정이 있습니다.

※ Killed Steel (킬드강, 탈산강)
Steel sufficiently deoxidized with ferrosilicon, aluminium, and so on.
In the case of ingot casting, during the progress of solidification in a ingot mold,
it is gently solidified without generation of carbon monoxide,
being comparatively uniform, with little segregation and has no blow hole.
however, because of a shrinkage cavity is formed in the centre of upper part,
its yield is low, In the case of continuous casting, it is killed steel and,
comparing with an ingot casting, uniformity and yield better.
killed steel is further classified according to grain size or deoxidizer.

페로실리콘이나, 알루미늄 등으로 충분히 탈산한 강철로,
용탕이 응고 진행 중에 일산화 탄소를 발생 시키지 않고,
조용히 응고해, 비교적 균질하고, 편석이 적고, 기포도 없지만
응고된 강괴 윗부분 중심으로부터, 수축공이 생겨, 회수율이
좋지 못한 단점이 있고, 결정 입도, 탈산제에 따라 세부적으로 더 분류됩니다.

※ 탄소강에서는 산소를 강철을 약하게 만드는 불순물로 보고
탈산제를 이용해 강(Steel) 내부의 산소를 제거함.

※ Fine grained steel (DIN-EN)
Steel with fine grain structure with an equivalent index of ferritic grain
size ≥ 6 determined in accordance with EN ISO 643

※ Fine grain steel
Steels which resist grain growth over a considerable temperature range,
when held at temperature for a reasonable length of time as is
customary in heat treatment of steel

※ 열처리( Heat Treatment : 熱處理)
철강재의 전체 또는 일부에 열 사이클을 적용하여 그 성질 또는 조직을 변화 시키는
일련의 작업으로, 철강재의 화학 조성은 이러한 작업 과정으로 변할 수 있습니다.

Series of operations in the course of which a solid ferrous product is totally or
or partially exposed to thermal cycles to bring about a change in its
properties and/or structure.
The chemical composition of the ferrous product may possibly be
modified during these operations.

API 5L Gr. L360Q, X52Q, PSL 2
Chemical composition (%)	Carbon (C)	0.18 max.
	Silicon (Si)	0.45 max.
	Manganese (Mn)	1.50 max.
	Phosphorus (P)	0.025 max.
	Sulfur (S)	0.015 max.
	Copper (Cu)	0.50 max.
	Chromium (Cr)	0.30 max.
	Nickel (Ni)	0.30 max.
	Molybdenum (Mo)	0.15 max.
	Titanium (Ti)	0.04 max.
	Vanadium (V)	0.05 max.
	Boron (B)	0.004 max.
	Nb+V+Ti	0.15 max.
Yield strength (MPa)		360~530
Tensile strength (MPa)		460~760
Elongation (%)		23 min.
PCM		25 max.
CEQ		43 min.
CVN Absorbed energy		Spec