C71640, CuNi B543 Heat Exchanger Tube

C71640, CuNi B543 Heat Exchanger Tube
STEELMAX Metal Story

C71640 동합금은 CuNi, CopperNickel 합금을 기본으로 하고
Iron (Fe), Manganese (Mn) 합금, 열교환기 튜브 규격입니다.

C71640 재질은 해양 미생물에 의한 biofouling (生物汚損) 저항성과
해수 부식에 좋은 저항성과 작업성이 좋은 금속입니다.

C71640 재질은 비중 8.94 g/㎤, Thermal conductivity 29.4 W/m·K,
Thermal expansion co-efficient at 20~300℃, 16.2чm/m℃ 성질입니다,

C71640 규격은 ASTM B111: SMLS Condenser Tube, B543 : Welded Heat
Exchanger Tube, B552 : SMLS and Welded Water Desalting Plants 용도로 구분됩니다.

70-30 Copper-Nickel (CuNi)/C71500 Modified 재질로, 국부 부식성에서는
약간 미치지 못하지만, 고속으로 흐르는 해수 (seawater) 부식에 더 강합니다.

※ Corrosion (부식 : 腐蝕)
Physicochemical interaction between a metal and its environment that results
in changes in the properties of the metal, and which may lead to significant
impairment of the function of the metal, or the technical system,
of which these form a part.
This interaction is often an electrochemical nature.

금속과 그 주변 환경의 물리 화학적 상호 작용으로 금속의 성질을
변하게 합니다. 이로 인해 금속, 환경 또는 기술 시스템 전체 또는
일부의 기능에 심각한 손상이 유발될 수 있습니다.
이 상호 작용은 간혹 전기 화학적인 특성을 나타냅니다.

※ 열전도율 (thermal conductivity : 熱傳導率)
물체 내에서 열에너지의 이동을 열전도도라고 하고 순 금속일수록
열전도율이 좋습니다. 20℃에서 열전도도가 가장 좋은 금속 은 (silver)
418.7 W/m·K, 니켈 (Ni) 92.1, 크롬 (Cr) 83.7 수준입니다.
공기, 나무는 열전도율이 낮고, 금속은 전도율이 높습니다.

※ 열팽창계수 (Thermal expansion coefficient)
온도(열)이 1℃ 상승할 때 팽창 된 크기와 팽창 전 크기의
비율을 말하고 선팽창계수와 부피 (체적) 팽창계수가 있습니다.

※ 냉간 가공 (Cold-working : 冷間加工)
가공 경화가 나타나는 온도에서의 금속 또는 합금의 소성 변형을 말합니다
Plastic processing method of metal or alloy which is carried out within such a
temperature range that strain hardening occurs.

※ Temper (질별 : 質別)
금속 또는 합금에 요구되는 특정한 물리적 및/또는 기계적 성질을
부여하는 공정으로 (예를 들어 기계적 처리 및/또는 열처리) 후의
제품의 상태를 말합니다.

C71640, ASTM B543, Density : 8.94 g/㎤
Chemical composition (%)	Copper (Cu)	remainder
	Nickel incl. Co	29.0~32.0
	Lead (Pb)	0.05 max
	Iron (Fe)	1.7~2.3
	Zinc (Zn)	1.0 max.
	Manganese (Mn)	1.5~2.5
	Carbon (C)	0.06 max
	Sulfur (S)	0.03 max
Temper : W061	Tensile strength (MPa)	435
Temper : W061	0.5% Yield strength (MPa)	170
Temper : WC55	Tensile strength (MPa)	515
Temper : WC55	0.5% Yield strength (MPa)	275

ASTM B543, Welded, Cu and Cu-Alloy Heat Exchanger Tube
UNS No.	Type of Metal	Temper Designation	Temper Name	Tensile strength (MPa)	0.5% Yield Strength (MPa)
C10800	Oxygen -free, Low Phosphorus	W061	Annealed	205	60
C10800	Oxygen -free, Low Phosphorus	WC55	Light Cold-Work	220	105
C12200	DHP Phosphorized, High	W061	Annealed	205	60
C12200	DHP Phosphorized, High	WC55	Light Cold-Work	220	105
C19400	Residual Phosphorus	W061	Annealed	310	105
C19400	Residual Phosphorus	WC55	Light Cold-Work	310	150
C23000	Red Brass	W061	Annealed	275	85
C23000	Red Brass	WC55	Light Cold-Work	290	140
C44300	Arcenical Admiralty	W061	Annealed	310	105
C44300	Arcenical Admiralty	WC55	Light Cold-Work	345	240
C44400	Antimonial Admiralty	W061	Annealed	310	105
C44400	Antimonial Admiralty	WC55	Light Cold-Work	345	240
C44500	Phosphorized Admiralty	W061	Annealed	310	105
C44500	Phosphorized Admiralty	WC55	Light Cold-Work	345	240
C68700	Arcenical Aluminum Brass	W061	Annealed	345	125
C68700	Arcenical Aluminum Brass	WC55	Light Cold-Work	agreed	agreed
C70400	95-5 Copper-Nickel	W061	Annealed	260	85
C70400	95-5 Copper-Nickel	WC55	Light Cold-Work	275	205
C70600	90-10 Copper-Nickel	W061	Annealed	275	105
C70600	90-10 Copper-Nickel	WC55	Light Cold-Work	310	240
C70620	90-10 Copper Nickel (modified for welding	W061	Annealed	275	105
C70620	90-10 Copper Nickel (modified for welding	WC55	Light Cold-Work	310	240
C71000	80-20 Copper-Nickel	W061	Annealed	310	110
C71000	80-20 Copper-Nickel	WC55	Light Cold-Work	345	240
C71500	70-30 Copper-Nickel	W061	Annealed	360	125
C71500	70-30 Copper-Nickel	WC55	Light Cold-Work	370	240
C71520	70-30 Copper Nickel (modified for welding	W061	Annealed	360	125
C71520	70-30 Copper Nickel (modified for welding	WC55	Light Cold-Work	370	240
C71640	Copper-Nickel-Iron-Manganese	W061	Annealed	435	170
C71640	Copper-Nickel-Iron-Manganese	WC55	Light Cold-Work	515	275
C72200	–	W061	Annealed	310	110
C72200	–	WC55	Light Cold-Work	345	205