AMS 6360, SMLS Tubing, SAE 4130, Aircraft Quality

2019-10-13T19:01:54+00:0010월 13th, 2019|

AMS 6360, SMLS Tubing, SAE 4130, Aircraft Quality
STEELMAX Steel Story

AMS 6360 재질은 Seamless Tubing 제품 규정으로, AISI-SAE 4130 과 대응됩니다.
Normalized or Stress Relieved 열처리된, 높은 강도와 내충격 성질이

요구되는 Aircraft Quality 재질로 저탄소 Chromium, Molybdenum 합금강재입니다.
Cold Drawn (냉간 인발) 제품인, 외경이 작은 0.499″ 이하부터

외경 12″ 까지, mechanical tubing, 원형 강관, 정각관, 직사각 강관 형태 제품입니다.
AMS 6360 재질은 Mil-T-6736B, AMS-T-6736, ASTM A519 Grade 4130 과 대응됩니다.

※ Stress Relieving(old name : stress relief annealing : 응력제거 어닐링(풀림)
Every piece of steel has an amount of internal stress caused
by steel production, machining, surface finish, heat treatment
and other processes.
During a heat treatment process the yield strength is reduced
to a lower level. If precision parts or complicated tools with
close tolerances, this deformation could cause problems.
In the case after rough machining and stress relieving is done
with a high degree of machining allowance.
After this process the internal stress is reduced by the parts deforming.
The standard process is slow heating up to 550~650℃, holding for
minimum 2 hours and finishing with a slow cooling in the furnace.

모든 철강재는 생산, 가공, 표면 마무리, 열처리와 기타 공정진행에서
내부 응력이 어느정도 쌓일 수 밖에 없고, 이런 내부 응력을 해소시키려고
적당한 온도로 가열하고 균열화한 후, 적절한 온도로 냉각함으로써
실질적인 조직의 변화없이 내부 응력을 줄이고자 시행하는 열처리를 말합니다.

※ Drawing (인발 : 引拔)
The process of pulling material through a die to reduce the size,
change the cross sectional shape, or to harden the material.

소재를 잡아 당겨, 다이를 통과시키면서 단면적이나 크기를
줄여나거나, 금속을 경화시키기도 하는 방법

※ Aircraft Quality Steel (AQ Steel : 항공기강 : 航空機鋼)
AQ Steel is the most commonly specified quality for general aerospace applications.
It is defined in SAE specification AMS 2301, which outlines the procedure for determining
compliance with cleanliness requirements by the magnetic particle inspection method.

A519 Grade 4130
Chemical composition (%) Carbon (C) 0.28~0.33
Manganese (Mn) 0.40~0.60
Silicon (Si) 0.15~0.35
Phosphorus (P) 0.030 max
Sulfur (S) 0.040 max
Chromium (Cr) 0.80~1.10
Molybdenum (Mo) 0.15~0.25

 

A519 Grade 4130 Typical Properties
Condition Ultimate Strength (MPa) Yield Strength (MPa) Elongation (%) Hardness (HRB)
Hot Rolled (HR) 855 621 15 100
Stress Relieved or Finish Anneal (SR) 855 689 10 100
Annealed (A) 552 414 25 85
Normalized (N) 855 621 20 100

 

AMS

AMS 6360, SMLS Tubing, SAE 4130, Aircraft Quality Steel

 

Carbon Steel, Special Steel, Stainless, Functional steel,
Ni-Alloy, Cu-Alloy, Al-Alloy, Ti-Alloy, Forging .

Plate, Sections, H-BEAM, Angle, Channel,
Flat, Round Bar, Rail, Pipe & Tube, SMLS,

ASTM, ASME, AISI, ANSI, API, SAE, AS, CSA
EN , KS, JIS, DNV, ABS, GL, LR, KR, NK. RINA, RS, CCA, IACS의

국가규격, 국제단체 규격, 국제협회 규격부터
Mill Maker Standards까지 공급하고 있습니다.

Citius, Altius, Fortius,
더 빠르게, 더 높이, 더 강하게가 요구되는  올림픽처럼

공급이 어려운 철강재 공급에는
진정한 전문 선수를 필요로 합니다.