SFCM880 Current, SFCM90S, Cr-Mo Forging

2019-10-31T09:21:55+00:0010월 31st, 2019|

SFCM880 Current, SFCM90S, Cr-Mo Forging Steel
STEELMAX Steel Story

SFCM880 재질은 Chromium, Molybdenum 합금강재입니다.
단조강으로 열처리로 강재의 강도를 조정하는 강재입니다.

SFCM880 — 현재사용 Steel Symbol, SFCM90 — 폐지된 규격으로
SFCM880 재질은 3가지로 나뉘어, SFCM880S/SFCM880R/SFCM880D 가 있습니다.

SFCM880S — Rods shapes, SFCM880R — Rings shapes
SFCM880D — Discs shapes, 3가지로 구분합니다.

KS D 4114, JIS G 3221 규정 재질로 이 규정 재질들은
QT 열처리하고, Tempering 온도는 500℃ 이상으로 합니다.

SNCM880 재질에서 Chromium 은 강재의 담금질성과 Temper 저항성을 높이고,
Molybdenum 은, Cr과 함께 하면 그 효과는 더 높아집니다.

※ Tempering (뜨임 열처리)
Heat treatment applied to a ferrous product, generally after quench hardening,
or another heat treatment to bring the properties to the required level, and
consisting of heating to specific temperature (<Ac1 )and soaking one or
more time, followed by cooling at an appropriate rate.
Tempering generally leads to a reduction in hardness
but can, in certain cases, cause an increase in hardness.

철강재를 퀜칭 경화 후, 또는 특정 수준의 성질을 얻기 위하여 (<Ac1 ) 온도
이하의 특정 온도로 가열한 후 한두 번 균열화한 다음, 적당한 속도로
냉각하는 별도의 열처리로
보통 템퍼링은 경도를 감소시키지만, 어떤 경우에는 도리어
경도가 증가할 수도 있습니다.

※ Quenched and Tempered Steel(QT, 조질강 : 調質鋼)
Steel products quenched and tempered in other to obtain
the properties which high strength steels should have.

퀜칭+템퍼링(담금질+뜨임) 열처리를 함으로서
고장력강으로서의 성질을 가지게한 강재.

SFCM880, SFCM90S, Cr-Mo Forging Steel
Currently Former
SFCM 590S SFCM 60S
SFCM 640S SFCM 65S
SFCM 690S SFCM 70S
SFCM 740S SFCM 75S
SFCM 780S SFCM 80S
SFCM 830S SFCM 85S
SFCM 880S SFCM 90S
SFCM 930S SFCM 95S
SFCM 980S SFCM 100S

 

SFCM880S, SFCM90S
Chemical composition (%) Carbon (C) 0.48 max
Silicon (Si) 0.15~0.35
Manganese (Mn) 0.30~0.85
Phosphorus (P) 0.030 max
Sulfur (S) 0.030 max
Chromium (Cr) 0.90~1.50
Molybdenum (Mo) 0.15~0.30
Yield Strength (MPa) d, t<200 655 min
200≤d, t<400 635 min
400≤d, t<700 625 min
Tensile Strength (MPa) 880~1030

 

Mechanical Properties Elongation (%) Reduction of Area (%) Impact Value (J) Hardness (HB)
Axial Tangential Axial Tangential Axial Tangential
d, t<200 13 min 39 min 49.0 min 255 min
200≤d, t<400 12 min 9 min 36 min 24 min 44.1 min 29.4 min
400≤d, t<700 11 min 8 min 33 min 22 min 39.2 min 24.5 min

 

KS-JIS 비교

SFCM880 Current, SFCM90S, Cr-Mo Forging Steel

 

스틸맥스는 연구소 수준의
깊이있는 철강에 대한 이해를 바탕으로,

Carbon Steel, Special Steel, Stainless, Functional,
Ni-Alloy, Cu-, Al-, Co-, Ti-, Mg-, Metal, Forging.

Plate, Sections, H-Beam, Round, Angle, Channel,
Rail, Crane Rail, Flat, I-Beam, Pipe & Tube, SMLS.

ASTM, ASME, AISI, API, SAE, AMS, KS, JIS, CSA,
DIN-EN, NORSOK, DNV, ABS, GL, LR, KR, NK, RS.