You are here:---LR LT-FH36-TM Z25, Low Temperature Steel

LR LT-FH36-TM Z25, Low Temperature Steel

2019-11-13T18:49:38+00:0011월 13th, 2019|

LR LT-FH36-TM Z25, Low Temperature Steel
STEELMAX Steel Story

 

LT-FH36 재질은 Low Temperature (저온용), High Strength (고장력)
36 kgf/㎟ (1 kgf/㎟ = 9.8 N/㎟ ) 강도의 (355 MPa minimum) 탄소강 강판입니다.

LT-FH36 저온용 고장력 탄소강 강판을 TMCP 방법으로 생산하면
LT-FH36-TM 으로 표기하고, LT-FH36-TM-Z25 로 표기되면

두께방향 인장시험 (Z-Direction) 이 있는 강재를 말합니다
LT-FH36 재질의 가장 큰 특징은 -60℃ 에서 저온충격 시험이 있습니다.

KS SM355C, EN 10025 S355J2 강재가 -20℃ 충격시험 온도와 비교하면
LT-FH36 재질의 -60℃ 는, 시험 온도가 훨씬 저온입니다.

저온으로 가면 갈수록 강재의 취성이 증가하므로, 저온환경에는
저온용 강재 (Low Temperature Steel) 가 사용됩니다.

※ Steels for low temperature service(저온용강재, 低溫用鋼材 : LTS 강재)
Steel products manufactured for the pressure vessels and structures
used at a low temperature which required toughness at a low
temperature and weldability.
There are carbon steel, low alloy steel, 2.5% nickel steel, 3.5 nickel steel
9% nickel steel, austenitic stainless steel, etc. according to use temperature.

저온하에서 쓰이는 용기설비 및 구조재로서 저온인성 및 용접성을 중시해서
제조된 강재로, 사용온도에 따라 탄소강, 저합금강, 2.5% 니켈강, 3.5% 니켈강
9% 니켈강, 오스테나이트 스테인레스강이 있습니다.

※ Transition temperature (천이온도 : 遷移溫度 or 전이온도 轉移溫度)
어떤 재료에 대해 여러 온도에서 충격시험을 하였을 때 흡수에너지가
급격히 저하(또는 상승) 하든가, 파면의 겉모양이 연성에서 취성으로
(또는 취성에서 연성) 변화하는 등의 현상에 대응하는 온도.
간단히 말해 충격치가 급변하는 온도, 저온취성을 나타내는 온도.

Temperature corresponding to the phenomenon in which absorbed
energy decreases (or increases) abruptly, or appearance of fracture
change from ductile to brittle(or from brittle to ductile) when impact
test at different temperature is conducted on a material.

 

 

LR LT-FH36 TMCP, Mill Test Certificate (MTC) Base
CVN Impact -60℃/284 joule
Yield Strength (MPa) 490
Tensile Strength (MPa) 588
Elongation (%) 21
Chemical Composition (%) Carbon (C) 0.07
Silicon (Si) 0.20
Manganese (Mn) 1.54
Phosphorus (P) 0.011
Sulfur (S) 0.002
Chromium (Cr) 0.030
Molybdenum (Mo) 0.015
Nickel (Ni) 0.220
Alunumum (Al) 0.019
Copper (Cu) 0.120
Nitrogen (N) 0.003
Titanium (Ti) 0.012
Niobium (Nb) 0.010
Vanadium (V) 0.002

 

Plate

LR LT-FH36-TM Z25, Low Temperature Steel

Plate

LR LT-FH36-TM Z25, Low Temperature Steel

 

스틸맥스는 연구소 수준의
깊이있는 철강에 대한 이해를 바탕으로,

Carbon Steel, Special Steel, Stainless, Functional,
Ni-Alloy, Cu-, Al-, Co-, Ti-, Mg-, Metal, Forging.

Plate, Sections, H-Beam, Round, Angle, Channel,
Rail, Crane Rail, Flat, I-Beam, Pipe & Tube, SMLS.

ASTM, ASME, AISI, API, SAE, AMS, KS, JIS, CSA,
DIN-EN, NORSOK, DNV, ABS, GL, LR, KR, NK, RS.

국가규격, 국제단체 규격, 국제협회 규격부터
Mill Maker Standards까지 공급하고 있습니다.