1.2355, 50CrMoV13-15, Shock Resistance

1.2355, 50CrMoV13-15, Shock Resistance
STEELMAX Steel Story

1.2355, 50CrMoV13-15 강재는 내충격강 (impact and shock resistance)
EN ISO 4957 Tool Steel 재질로, 고온에서도 연화 저항성 강재입니다.

냉간 (cold work), 열간 (hot work) 공정에 모두 사용 가능하고
높은 인성과 내마모성, 치수 안정성, 좋은 경면 (polishability) 가능합니다.

EN ISO 1.2355, 50CrMoV13-15 재질은 DIN 1.2357,50CrMoV13-14
ASTM A681 S7 재질과 대응 가능하고, 비교 가능한 KS 재질은 없습니다

QT 열처리시에는 56 HRC minimum, Annealed HB 248 max 입니다.
chisels, hot punching and shearing, shear blades 용도로 쓰입니다.

※ Alloy Tool Steel (합금 공구강 : 合金工具鋼)
Tool steels used in which one or more alloy elements such as silicon,
manganese, nickel, chromium, molybdenum, tungsten, vanadium, etc.
are added in carbon steels.
They are steels which improved on carbon tool steels in hardenability,
machinability, shock resistance, abrasion resistance, non-deformability,
heat resistance, etc., as required. They are classified into cutting tool,
impact resistance tool, cold mold tool and hot roll mold categories by usage.

탄소강에 망간, 니켈, 크롬, 몰리브덴, 텅스텐, 바나듐 등의 합금 원소를
1종이상 첨가한 공구강으로, 탄소 공구강에 대해서 경화성, 절삭 성능
내충격성, 내마모성, 불변형성, 내열성 등을 필요에 따라 개선한 강재입니다.

※ Cold-work tool steels (냉간 공구강 : 冷間工具鋼)
Non-alloy and alloy tool steels for applications in which
the surface temperature is generally below 200℃.

표면 온도가 200℃ 이하의 분야에 적용되는 비합금 또는 합금 공구강.

※ Hot-work tool steels (열간 공구강 : 熱間工具鋼)
Alloy tool steels for applications in which the surface temperature
is generally over 200℃.
표면 온도가 200℃ 초과하는 분야에 적용되는 합금 공구강.

1.2355, 50CrMoV13-15
Chemical composition (%)	Carbon (C)	0.45~0.55
	Silicon (Si)	0.20~0.80
	Manganese (Mn)	0.50~0.90
	Chromium (Cr)	3.00~3.50
	Molybdenum (Mo)	1.30~1.70
	Vanadium (V)	0.15~0.35
Hardness	Annealed (HB)	248 max
Hardness	+QT (HRC)	56 min