AMS-S-7108 규정은 Mn-Si-Ni 합금강재로 Bars and Forgings
항공기강 (aircraft quality)으로 열처리시 인장강도 최소 1518 MPa 강재입니다.

AMS-S-7108 강재는 높은 강도와 파괴인성, 좋은 연성 강재로
Aircraft landing gear, flap tracks and other structural applications 용도입니다.

AMS-S-7108 강재는 AMS 2301 규정인, 강의 청정성(cleanliness)을 확보하기 위한
항공기강의 비파괴시험인,  자분탐상 (magnetic particle) 시험이 있습니다.

AMS-S-7108 강재는 UNS K32550, Boeing DMS-1841
GE-S-400 S-1000 규정과 대응 가능한 저합금강재입니다.

※ Toughness (인성 : 靭性)
The degree of difficulty in occurring impact breaking
because of the material’s toughness .
질기고 세며, 충격파괴를 일으키기 어려운지, 어떤지의 정도.

※ Ductility(연성 : 延性)
The property of metals that enables them to be mechanically deformed
when cold, without fracture. In steel, ductility is usually measured by
elongation and reduction area is determined in a tensile test.

금속에 인장력을 줘 소성변형을 일으켰을 때, 끊어짐이 없이 선(line)상으로
늘릴 수 있는 성질을 연성이라고 하고, 연성은 인장시험에서
연신율(Elongation), 단면수축율(Reduction area; RA)로 측정합니다.
물질이 파괴되지 않고 유연하게 변할 수 있는 능력입니다.
쉽게 말해 물질이 파괴되지 않고 유연하게 변형할 수 있는 능력입니다.

※ Heat Treatment (열처리)
Normalizing Temperature : 940℃ (1725℉), 1h, air cool
Austenitizing Temperature (Hardening Temperature) : 871℃(1600℉), 1h, oil quench
Tempering Temperature : 550℉ (288℃) : 2h, air cool

※ Special Aircraft Quality Steel (특수 항공기강 : 特殊 航空機鋼)
SAQ Steel level of quality places minimum values on ductility in the transverse direction.
It is also known as “High Transverse Quality” as the steel is evaluated by the number of
tension tests normal to the direction of rolling (transverse) performed to obtain a
comprehensive sampling of a heat of steel.

AMS-S-7108, AMS 2301
Chemical composition (%) Carbon (C) 0.23~0.28
Manganese (Mn) 1.20~1.50
Phosphorus (P) 0.025 max
Sulfur (S) 0.025 max
Silicon (Si) 1.30~1.70
Chromium (Cr) 0.20~0.40
Nickel (Ni) 1.65~2.00
Molybdenum (Mo) 0.35~0.45
Yield Strength (MPa) 1277 min
Tensile Strength (MPa) 1518~1690
Elongation (%) 5 min
Reduction of Area(%) Average 20 min
Single 15 min

 

AMS

AMS-S-7108, K32550, AMS 2301, Aircraft Steel

 

스틸맥스는 연구소 수준의
깊이있는 철강에 대한 이해를 바탕으로,

Carbon Steel, Special Steel, Stainless, Functional,
Ni-Alloy, Cu-, Al-, Co-, Ti-, Mg-, Metal, Forging.

Plate, Sections, H-Beam, Round, Angle, Channel,
Rail, Crane Rail, Flat, I-Beam, Pipe & Tube, SMLS.

ASTM, ASME, AISI, API, SAE, AMS, KS, JIS, CSA,
DIN-EN, NORSOK, DNV, ABS, GL, LR, KR, NK, RS.

국가규격, 국제단체 규격, 국제협회 규격부터
Mill Maker Standards까지 공급하고 있습니다.

Citius, Altius, Fortius,
더 빠르게, 더 높이, 더 강하게가 요구되는 올림픽처럼

공급이 어려운 철강재 공급에는
진정한 전문 선수를 필요로 합니다.