Chronifer® M15KL, F899 420 Mod, AISI 420 Mod

Chronifer® M15KL, F899 420 Mod, AISI 420 Mod
STEELMAX Steel Story

Chronifer® M-15KL 재질은 Martensitic Stainless 재질입니다.
청정강을 제조하는 ESR (Electro Slag Remelting) 제조하며

특히 낮은 Sulfur (황) — 0.005% maximum 수준의 강재입니다.
의료용으로 사용되는 스텐 도구를 만드는 데의 소재로 사용됩니다.

같은 Martensitic 스텐레스 AISI 440C, 440B, 440A 보다는
탄소량이 적어, 좋은 내식성 재료입니다.

Chronifer® M15KL 재질을 예리하게 만들면, 쉽게 날이 뭉툭해지지 않으며
좋은 내마모성과 mirror 급의 표면 마무리가 가능합니다.

Chronifer® M15KL 재질은 담금질 후 2차 담금질과Sub-zero 심랭 처리로
잔류 오스테나이트를 제거하고 마르텐자이트 조직을 얻습니다.

Chronifer® M-15KL 재질은, ASTM F899– Standard Specification
for Wrought Stainless Steels for Surgical Instruments, 420 Mod,

AMS 5925 : Steel, Corrosion Resistant, Bars, Wire, and Forgings
15.5Cr-1.8Mo-0.20N (0.37~0.45C) Electroslag Remelting 재질에 대응됩니다.

※ Sub-zero treating (심냉 처리, deep freezing)
Treatment carried out after quenching to transform the retained
austenite into martensite and consisting of cooling to and soaking
at a temperature below ambient
The sub-zero cooling is done between -60 and -196℃

담금질 후 상온 이하의 온도로 냉각해 균열화 함으로서 잔류 오스테나이트를
마르텐자이트로 변태 시키기 위해 시행하는 처리를 말합니다.
심랭 처리는 -60 ~ -196℃ 수준에서 처리합니다.

※ ESR (Electro Slag Remelting : 일렉트로 슬래그 재 용해)
After casting, the ingot is remelted from bottom to top by electric energy,
During this process, the melted steel falls through slags, which collects
almost all of the non-metallic inclusions
A new ingot solidifies from bottom to top and there is very little segregation
from case to core.
The fatigue resistance and in particular the toughness increase.
Even through ESR increases material costs, it can still be economical due to
the increase in the tool’s performance.
Metal injection moulds and extrusion dies often need ESR steel grades.

ASTM F899 420 Mod, AISI 420 Mod
Chemical composition (%)	Carbon (C)	0.37~0.45
	Manganese (Mn)	0.60 max
	Phosphorus (P)	0.02 max
	Sulfur (S)	0.005 max
	Silicon (Si)	0.60 max
	Chromium (Cr)	15.00~16.50
	Molybdenum (Mo)	1.50~1.90
	Vanadium (V)	0.20~0.40
	Nitrogen (N)	0.16~0.25
Typical Hardness at Indicating Tempering Temp.	350℉/177 ℃	56/57 HRC
	400℉/204 ℃	55 HRC
	500℉/260 ℃	54 HRC
	600℉/315 ℃	53 HRC
1900℉(1010℃)+oil quench or pressure gas

420 Mod Usages Accordance with ISO 7153/1
Cutting Instruments	Non-Cutting Instruments
bone rongeurs, conchotomes, bone cutting forceps, chisels and gouges, bone curettes, scissors with carbide inserts, scissors, scalpels, knives	tissue forceps, dressing forceps, retractors, probes, forceps, forceps with bow handles, branch forceps