X19CrMoNbVN11-1, 1.4913, Creep-Resisting Steel

X19CrMoNbVN11-1, 1.4913, Creep-Resisting Steel
STEELMAX Steel Story

X19CrMoNbVN11-1 이라는 길고 긴, Material Name과
1.4913, Material Number 를 가지는, DIN-EN 10302,

Steels and nickel alloys for bars and rods for fasteners with
properties specified at elevated and/or low temperature made

of non-alloy (including stainless) steels and nickel alloys,
규정 안에 있는 강종입니다.

합금 화학 원소 — Chemical composition,
열처리별 기계적 성질 — Mechanical properties at room temperature

온도 구역별 항복 강도 — Minimum 0.2% proof strength value at elevated temperature
비중과 정탄성계수 — Density(7.7) and static modulus of elasticity

열팽창계수 — Coefficient of thermal expansion
열전도율 — Thermal conductivity

열 용량과 전기 저항율 — Thermal capacity and electrical resistivity
크리프 강도 — Strength values for 1% creep strain and creep rupture

다양한 금속, 철강 관련 규정을 가지는, 11% Chromium 합금,
QT, Annealing 열처리, 고온용 강재 입니다.

※ Creep rupture test
Test measure the time to rupture, elongation after fracture,
reduction of area after fracture, etc. by holding test piece
at constant temperature and applying constant tensile force.
There are at times the cases where strain is measured during
creep rupture test or by interrupting test.

시험편을 일정한 온도로 유지하고 여기에 일정한 인장 하중을 가해,
파단 시간, 파단 연신율, 파단 단면 수축율 등을 측정하는 시험.
크리프 파단 시험 중 또는 시험을 중단하여
변형을 측정하는 경우도 있습니다.

※ Creep strength
Stress to cause specified strain in specified loading period of
time at constant temperature.
For example, the stress causing strain 1%, 0.1%, 0.01% in 1000h.

일정 온도하에서, 규정된 부하 시간에 규정된 변형이 생기는 응력.
예를 들면 1000 시간에 1%, 0.1% 또는 0.01%의 변형이
생기는 응력이 사용됩니다.

X19CrMoNbVN11-1, 1.4913, Creep-Resisting Steel