X10CrAlSi7, 1.4713, Ferritic Heat-Resisting Steel

X10CrAlSi7, 1.4713, Ferritic Heat-Resisting Steel
STEELMAX Steel Story

X10CrAlSi7, 1.4713, Chromium 합금
Ferritic 내열강재입니다.

황을 포함한 가스에 저항성이 커, 로 (Furnace : 爐)에 사용되며
800℃ 정도의 내 고온성을 가지고, 탄화속도가 아주 느립니다.

1.0% Proof strength (항복 강도) : 220 MPa minimum
Tensile strength (인장 강도) : 420~620 MPa

Hardness HB (경도)  : 192 maximum.
Longitudinal elongation (압연 방향 연신율): 20% minimum 입니다.

※ Heat resisting steels
Alloy steels which retain oxidation resistance, high temperature
corrosion resistance or high temperature strength under
various circumstances at high temperature.
They often contain nickel, cobalt, tungsten and/or other alloy
elements other then several % min of chromium.
Principally, they are classified into four types, which are
martensitic, ferritic, austenitic and precipitation hardening,
according to their structure.
Further, when total amount of alloy elements exceed about
50%, they are generally, called super alloy, heat resisting
alloy or super heat resisting alloy.

내열강이란 고온에서의 각종 환경에서 내산화성,
내고온 부식성 또는 고온 강도를 유지하는 합금강으로
수% 이상의 크롬 외에 니켈, 코발트, 텅스텐 등
합금 원소를 함유하는 경우가 많으며
내열강은 그 금속의 조직에 따라
마르텐사이트계, 페라이트계
오스테나이트계, 석출경화계, 4가지로 분류됩니다.
또한 합금 원소의 총량이 50%를 넘는 경우는
초내열 합금, 또는 내열 합금, 또는 간단히
초합금이라고 부릅니다.

※ Hardness (경도 : 硬度)
Resistance to plastic deformation usually by indentation.
For steel users, it is a parameter to express different mechanical
properties of steel. It should be considered together with other
properties. For example, if two different steel grades have both
50 HRC hardness, it does not necessary mean both have the
same mechanical properties or wear resistance.

압인이나 긁힘에 의한 변형, 특히 영구적인 변형에 대한 재료의
내구성으로 강재의 기계적 성질의 지표입니다.
다른 강재가, 같은 경도 값을 가지더라도 내마모성, 기계적 성질이
다를 수 있으니, 경도와 함께 다른 기계적 성질도 참고해야 합니다.

X10CrAlSi7, 1.4713, Ferritic Heat-Resisting Steel