AMS 5662, Alloy 718, N07718 B637 Ni-Based Super-Alloy

AMS 5662, Alloy 718, N07718 B637, B670 Nickel-Based Super-Alloy
STEELMAX Steel Story

Alloy 718 은, Nickel 함량만 50~55% 수준의
Nickel-based super-alloy 입니다.

980℃ 에서의 내산화성–Oxidation resistance,
700℃ 이상 온도에서 크립 강도 — Creep resistance

1000 MPa 이상의 항복 강도 — High yield strength
특성을 가지는 AMS 5662, Nickel Alloy 718 금속이며

내식성 — Corrosion resistance,
특성이 이러다 보니, 사용되는 환경은

고온용 볼트 — High temperature bolts and fasteners
고속 항공기용 기체 부품 — High speed air-frame parts

항공기 터빈 하우징 — Aircraft turbines housing
회전 부품 — Rotating components 으로 사용됩니다.

관련 Specification 으로는
AMS 5662 : Inconel 718 Nickel Alloy, Corrosion & Heat Treatment, Bars

Rings, Consumable Electrode Remelted or Vacuum Induction Melted,
Solution Heat treated, Precipitation-Hardenable.

AMS 5596, AMS 5597 : Sheet, Strip and Plate
AMS 5589, AMS 5590 : Seamless Tube.

ASTM B637 N07718 : Bars, Forgings
ASTM B670 N07718 : Plate, Sheet, Strip.

B637 UNS N07718, Solution+PH
Chemical composition (%)	Nickel (Ni)	50.0~55.0
	Chromium (Cr)	17.0~21.0
	Cb(Nb)+Ta	4.75~5.50
	Molybdenum (Mo)	2.80~3.30
	Cobalt (Co)	1.0 max
	Titanium (Ti)	0.65~1.15
	Iron (Fe)	remainder
	Carbon (C)	0.08 max
	Manganese (Mn)	0.35 max
	Silicon (Si)	0.35 max
	Phosphorus (P)	0.015 max
	Sulfur (S)	0.015 max
	Aluminum (Al)	0.20~0.80
	Copper (Cu)	0.30 max
	Boron (B)	0.006 max
Strength	Tensile (MPa)	1275 min
Strength	Yield (MPa)	1034 min
Elongation (%)		12 min
Reduction of area (%)		15 min
Hardness (HB)		331 min

※ Heat resisting steels
Alloy steels which retain oxidation resistance, high temperature
corrosion resistance or high temperature strength under
various circumstances at high temperature.
They often contain nickel, cobalt, tungsten and/or other alloy
elements other then several % min of chromium.
Principally, they are classified into four types, which are
martensitic, ferritic, austenitic and precipitation hardening,
according to their structure.
Further, when total amount of alloy elements exceed about
50%, they are generally, called super alloy, heat resisting
alloy or super heat resisting alloy.

내열강이란 고온에서의 각종 환경에서 내산화성,
내고온 부식성 또는 고온 강도를 유지하는 합금강으로
수% 이상의 크롬 외에 니켈, 코발트, 텅스텐 등
합금 원소를 함유하는 경우가 많으며
내열강은 그 금속의 조직에 따라
마르텐사이트계, 페라이트계
오스테나이트계, 석출경화계, 4가지로 분류됩니다.
또한 합금 원소의 총량이 50%를 넘는 경우는
초내열 합금, 또는 내열 합금, 또는 간단히
초합금이라고 부릅니다.