AISI 8630, AMS 8630 는 저합금 강재 입니다.
Nickel, Chromium, Molybdenum 저합금강재이면서

탄소량이 0.30% 수준으로 높지 않습니다.
AISI 8630, 환봉, 단조강, Pipe 제품으로 제조 되며

좋은 기계적 성질을 가지며, 열처리로는, Annealing,
Quenching and Tempering, Normalizing 를

해서 사용하며, 열처리 조건에 따라서
강도와 연신율, 경도가 달라집니다.

AISI 8630, 침탄 (Carburized)으로
경도를 높여 사용하기도 합니다.

Gears, Shafts, Crankshafts,
Ring gear 로, 사용됩니다.

※ AMS 8620 : Aircraft-quality, low-alloy steel in the form of bars,
forgings, flash welded rings, and stock forging or flash welded rings.

※ Case hardening steel (표면 경화강: 表面硬化鋼)
Low carbon steels and low carbon alloy steels of machine structural use
whose surfaces are hardened mainly by carburization hardening…….…JIS
Steels with a relatively low carbon content, which are intented for
carburizing or carbonitriding and subsequent hardening.
Such steels, after treatment, are characterized by a high hardness
surface layer and a tough ….…DIN-EN.

저탄소강 및 저탄소 합금강으로, 주로 침탄 퀜칭에 의해 표면 경화 시킨 강
표면의 내마모성과 내피로성을 높이지만, 강재 내부의 인성을 유지 시킨 강재.
표면 경화 방법으로는 침탄 (Carburizing), 질화 (Nitriding), 침붕 (Boriding)이 있고
각각 탄소, 질소, 붕소를 강재 표면에 침투 시켜 경화 시키는 방법입니다.

※ Carburizing (침탄 : 浸炭)
Thermochemical treatment which is applied to a ferrous product heated
to a temperature AC1, to obtain a surface enrichment in carbon and
nitrogen, which are in solid solution in the austenite.
Generally, this operation is followed immediately by quench hardening.
The medium in which carbonitriding takes place should be specified,
e.g. gas, salt bath, etc.

오스테나이트 상태의 철강재에서 표면에만 오스테나이트 중의 고용 탄소의
농도를 높이고자 시행하는 열 화학적 처리로, 침탄 된 철강재는 그 즉시 또는
이후에 급랭 담금질 처리가 뒤따라야 하며, 침탄에 이용한  가스나 고체 등의
매질 표시가 반드시 표기되어야 합니다.