CA6NM, ASTM A743, Casting Stainless Steel

CA6NM, ASTM A743, Casting Stainless Steel
STEELMAX Steel Story

CA6NM, ASTM A743 은 Casting (주물 제품)입니다.
Chromium 13% 수준에 Ni, Mo 합금, 스테인레스 입니다.

NT 열처리에 의해 (Normalizing and Tempering)
높은 인장강도 — 755 MPa minimum,

높은 항복강도 — 550 MPa minimum 입니다.
탄소량은 0.06% maximum 으로 저탄소 입니다.

CA6NM, ASTM A743 은 염수에 대한
내식성(salt water corrosion resistance) 금속입니다.

Use for ship propellers, water turbine components,
pump castings, concast rollers 로 사용됩니다.

A743/A743M Standard Specification for Castings, Iron-Chromium,
Iron-Chromium-Nickel, Corrosion Resistant, for General Applications.

ASTM A743 CA6NM
Chemical composition(%)	Carbon (C)	0.06 max
	Manganese (Mn)	1.00 max
	Silicon (Si)	1.00 max
	Phosphorus (P)	0.04 max
	Sulfur (S)	0.03 max
	Chromium (Cr)	11.5~14.0
	Nickel (Ni)	3.5~4.5
	Molybdenum (Mo)	0.40~1.0
Tensile strength (MPa, min)		755
Yield strength (MPa, min)		550
Elongation (%, min)		15
Reduction area (%, min)		35

※ Steel castings (주강품 : 鑄鋼品)
Steels cast into mold to obtain the desired shape.
For mold, there are sand mold, metal mold, fire brick, black lead and so on.

강철을 주형에 주입해 소요 제품의 모양으로 만든 것으로
사형 (沙型), 금속 주형, 적벽돌 주형, 흑연 주형 등이 있습니다.

※ Centrifugal steel castings (원심력 주강품 : 遠心鑄鋼品)
Steel castings manufactured by centrifugal casting
For the rotating shaft, vertical and horizontal type, and
for mold, there metal mold and sand mold.

원심력 주조법으로 제조 된 주강품.
회전의 축 방향에 따라서 직립형과 수평형이 있으며
주형으로는 금형과 사형 (沙型)이 있습니다.